PremierCap® 1852

PremierCap® 1852 is a next-generation high gloss, co-extruded cap over a high stiffness, talc-filled TPO core. This product is designed to offer a weatherable cap that provides enhanced scratch & mar resistance over a structural substrate with high flex modulus and heat deflection temperature properties.

Applications

  • Exterior components
  • Industrial covers
  • Housings
  • Hoods
  • Claddings
  • Shrouds
  • Structural Parts

Properties

  • Property Typical Value Units Test Method
  • Specific Gravitiy 1.15 ISO 1183
  • Gloss, 60°
    (smooth, post-formed, male tooling)
    85 - 90 % ASTM 523
  • Crock Mar Resistance
    (Retained gloss at °60 observer)
    75-80 % PMC Method
  • Shrink Rate 0.8 – 1.0 % ISO 294-4
  • Flexural Modulus 540,000
    3,724
    psi
    MPa
    ASTM D790
  • Tensile Strength at Yield 4,200
    29
    psi
    MPa
    ASTM D638
  • Gardner Impact at 32°F (0°C)
    at -22°F (-30°C)
    280 (31.2)
    142 (15.8)
    in*lbs (Joules) ASTM D5420
  • HDT at 66 psi (0.45 MPa)
    at 264 psi (1.45 MPa)
    235(110)
    142(61)
    °F (°C) ASTM D648
  • CLTE (-30°C to 80°C) 3.2 x 10-5
    5.8 x 10-5
    in/in/°F
    mm/mm/°C
    ISO 11359

*Property values tested on co-extruded sheet, 0.187” thick, 10% cap layer, 30% regrind.157”) thick, 10% cap layer, 30%

NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.