PMC® 815 is 22% glass filled TPO core sheet, capped with a standard melt strength, talc-filled TPO. This combination provides the enhanced stiffness & HDT of the glass-filled TPO, with improved surface aesthetics over a monolithic glass filled sheet. Available in multiple colors and in a variety of textures.

Applications

  • Industrial covers
  • Structural housings
  • Fan shrouds

Properties

  • Property Typical Value Units Test Method
  • Specific Gravitiy 1.06 - 1.08 ISO 1183
  • Hardness 76 - 78 Shore D ISO 868
  • Gloss, 60°
    (textured, post-formed, male tooling)
    10 - 15 % ASTM 523
  • Shrink Rate 0.6 – 0.8 % ISO 294-4
  • Flexural Modulus 536,000
    3,700
    psi
    MPa
    ASTM D790
  • Tensile Strength at Yield 9,280
    64
    psi
    MPa
    ASTM D638
  • Notched Izod at 23°F (-5°C) 40
    85
    ft*lb/in2
    kJ/m2
    ASTM D256
  • HDT at 66 psi (0.45 MPa)
    at 264 psi (1.45 MPa)
    293(145)
    269(132)
    °F (°C) ASTM D648
  • CLTE (-30°C to 80°C) 3.3 x 10-5
    5.9 x 10-5
    in/in/°F
    mm/mm/°C
    ISO 11359

 

NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.