PremierCap® 1750

PremierCap® 1750 is a co-extruded TPO sheet system designed to offer a high gloss, excellent scratch & mar resistant, weatherable cap over a performance substrate that resolves environmental “whitening” found in traditional monolithic talc-filled TPO, with broader processing window, and favorable mechanical properties.

Applications

  • Exterior components
  • Industrial covers
  • Housings
  • Claddings
  • Shrouds

Properties

  • Property Typical Value Units Test Method
  • Specific Gravitiy 1.10 ISO 1183
  • Gloss, 60°
    (smooth, post-formed, male tooling)
    85 - 90 % ASTM 523
  • Crock Mar Resistance
    (Retained gloss at °60 observer)
    75-80 % PMC Method
  • Shrink Rate 0.8 – 1.0 % ISO 294-4
  • Flexural Modulus 290,800
    2,006
    psi
    MPa
    ASTM D790
  • Tensile Strength at Yield 3,091
    21.3
    psi
    MPa
    ASTM D638
  • Gardner Impact at 32°F (0°C)
    at -22°F (-30°C)
    320 (36)
    208 (23)
    in*lbs (Joules) ASTM D5420
  • Multi-Axial Impact at 32°F (0°C)
    at -5°F (-15°C)
    at -22°F (-30°C)
    44.0, 100% ductile
    32.4, 50% ductile
    Joules ASTM D3762
  • HDT at 66 psi (0.45 MPa)
    at 264 psi (1.45 MPa)
    212(100)
    134(57)
    °F (°C) ASTM D648
  • CLTE (-30°C to 80°C) 3.3 x 10-5
    5.9 x 10-5
    in/in/°F
    mm/mm/°C
    ISO 11359

*Property values tested on co-extruded sheet, 0.187” thick, 10% cap layer, 30% regrind.157”) thick, 10% cap layer, 30%

NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.