PMC® 700

PMC® 700 is a monolithic TPO sheet comprised of a high melt strength, impact-modified, talc-filled TPO, to achieve a broader processing window, while maintaining favorable mechanical properties.

Applications

  • Bumpers
  • Wheel lips
  • Valences
  • Claddings
  • Rocker panels
  • Industrial covers & enclosures

Properties

  • Property Typical Value Units Test Method
  • Specific Gravitiy 1.12 ISO 1183
  • Gloss, 60°
    (textured, post-formed, male tooling)
    7 - 10 % ASTM 523
  • Shrink Rate 0.7 – 0.9 % ISO 294-4
  • Flexural Modulus 300,150
    2,070
    psi
    MPa
    ASTM D790
  • Tensile Strength at Yield 3,450
    23.8
    psi
    MPa
    ASTM D638
  • Gardner Impact at 32°F (0°C)
    at -22°F (-30°C)
    322(36)
    316(35)
    in*lbs (Joules) ASTM D5420
  • Multi-Axial Impact at -32°F (0°C)
    at -22°F (-30°C)
    45.4, 100% ductile
    51.1, 100% ductile
    Joules ASTM D3763
  • HDT at 66 psi (0.45 MPa)
    at 264 psi (1.45 MPa)
    214 (101)
    138 (59)
    °F (°C) ASTM D648
  • CLTE (-30°C to 80°C) 3.1 x 10-5
    5.5 x 10-5
    in/in/°F
    mm/mm/°C
    ISO 11359

 

NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.