PMC® 650

PMC® 650 is a coextruded, standard melt strength, TPO sheet system with an olefinic high gloss cap layer.

Applications

  • Exterior Components
  • Industrial Covers
  • Valences
  • Claddings
  • Rocker Panels
  • Shrouds
  • Radomes

Properties

  • Property Typical Value Units Test Method
  • Specific Gravity 1.10 ISO 1183
  • Gloss, 60°
    (smooth, post-formed, male tooling)
    85 - 90 % ASTM 523
  • Shrink Rate 0.8 - 1.1 % ISO 294-4
  • Flexural Modulus 266,400
    1,837
    psi
    MPa
    ASTM D790
  • Tensile Strength at Yield 2,598
    17.9
    psi
    MPa
    ASTM D638
  • Gardner Impact at 32°F (0°C)
    at 22°F (-30°C)
    320 (36)
    280 (23)
    in*lbs (Joules) ASTM D5420
  • Multi-Axial Impact at -22°F(-30°C) 28.0, 100% ductile Joules ASTM D3762
  • HDT at 66 psi (0.45 MPa)
    at 264 psi (1.45 MPa)
    210 (99)
    127 (53)
    °F (°C) ASTM D648
  • CLTE (-30°C to 80°C) 3.3 x 10-5
    5.9 x 10-5
    in/in/°F
    mm/mm/°C
    ISO 11359

*Property values tested on co-extruded sheet, 0.125 in (4 mm) thick, 10% cap layer, 30% regrind used

NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.