PMC® 310

PMC® 310 is a co-extruded low gloss ABS cap extruded over a high-impact ABS core, offering good impact resistance in applications where an ultra-low gloss A-surface is desired.

Applications

  • Interior components
  • Instrument dash panels
  • Door trim
  • Housings & claddings

Properties

  • Property Typical Value Units Test Method
  • Hardness 77 Shore D ASTM D2240
  • Specific Gravity 1.05 ISO 1183
  • Gloss, 60°
    (textured*, post-formed, male tooling)
    <5 % ASTM 523
  • Shrink Rate 0.4 – 0.6 % ISO 294-4
  • Flexural Modulus 310,000
    2,138
    psi
    MPa
    ASTM D790
  • Tensile Strength at Yield 4,800
    33
    psi
    MPa
    ASTM D638
  • Gardner Impact
    at 73°F (23°C)
    at 32°F (0°C)
    at -22°F (-30°C)
    192(22)
    204(23)
    218(25)
    in*lbs(Joules) ASTM D638
  • HDT at 66 psi (0.45 MPa)
    at 264 psi (1.45 MPa)
    195 (91)
    180 (82)
    °F (°C) ASTM D648
  • CLTE (-30°C to 80°C) 4.8 x 10-5
    8.6 x 10-5
    in/in/°F
    mm/mm/°C
    ISO 11359
  • Burn Rate 41 mm/min FMVSS302

* Textured gloss noted. Non-textured (smooth) use of this product not recommended. Color & Texture can affect post-formed gloss rating. Property values tested on monolithic extruded sheet, 0.180 in. (4.6 mm) thick, 30% regrind used.

NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.