PremierCap® 1520
PremierCap® 1520 is a next-generation low gloss, coextruded TPO sheet system over a high recycle content core. This product is designed to offer a weatherable cap that provides enhanced scratch & mar resistance over a cost-effective substrate, providing enhanced surface durability with improved economics.
Applications
- Exterior components
- Industrial covers
- Housings
- Claddings
- Shrouds
Properties
- Property Typical Value Units Test Method
- Specific Gravity 1.06 – 1.08 ISO 1183
- Gloss, 60°
(smooth, post-formed, male tooling) 14 – 18 % ASTM 523 - Crock Mar Resistance
(Retained gloss at 60° observer) 75 - 80 % PMC Method - Shrink Rate 0.9 – 1.1 % ISO 294-4
- Flexural Modulus 260,000
1,792 psi
MPa ASTM D790 - Tensile Strength at Yield 2,800
19.3 psi
MPa ASTM D638 - Gardner at 32°F (0°C)
Impact at -22°F (-30°C) 320 (36.2)
313 (35.0) in*lbs (Joules) ASTM D5420 - HDT at 66 psi (0.45 MPa)
at 264 psi (1.45 MPa) 187 (86)
116 (47) °F (°C) ASTM D648
1 Property values based on a combination of sheet and raw material plaque testing
NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.