PremierCap® 1620 is a next-generation low gloss, coextruded TPO sheet system over a standard melt strength core. This product is designed to offer a weatherable cap that provides enhanced scratch and mar resistance over a cost-effective substrate, providing enhanced surface durability with improved economics.

Applications

  • Exterior Components
  • Industrial Covers
  • Housings
  • Claddings
  • Shrouds

Properties

  • Property Typical Value Units Test Method
  • Specific Gravity 1.06 ISO 1183
  • Gloss, 60° (smooth, post-formed, male tooling) 14 - 18 % ASTM 523
  • Crock Mar Resistance (retained gloss at 60° observer) 70 - 80 % PMC Method
  • Shrink Rate 0.9 - 1.1 % ISO 294-4
  • Flexural Modulus 250,000 (1,724) psi (MPa) ASTM D790
  • Tensile Strength at Yield 2,740
    18.9     psi
    MPa     ASTM D638
  • Gardner Impact at 32°F (0°C)
    at -22°F (-30°C)     320 (36.2)
    313 (35)     in*lbs (Joules) ASTM D5420
  • Multi-Axial Impact at 32°F (0°C)
    at -5°F (-15°C)
    at -22°F (-30°C)     28.2, 100% ductile
    41.0, 100% ductile
    18.7, 0% ductile     Joules ASTM D3762
  • HDT at 66 psi (0.45 MPa)
    at 264 psi (1.45 MPa)     189 (87)
    118(48)     °F (°C) ASTM D648
  • CLTE (-30°C to 80°C) 3.4 x 10-5
    6.9 x 10-5     in/in/°F
    mm/mm/°C     ISO 11359

Property values tested on coextruded sheet, 0.125 in thick, 10% cap layer, 30% regrind

NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.