PremierCap® 1755

Request a Sample Place an Order Submit a Color Match

Downloads

PremierCap® 1755 is a next-generation high gloss, co-extruded TPO sheet system over an ultra-high melt strength core. This product is designed to offer a weatherable cap that provides enhanced scratch & mar resistance over a performance substrate with the broadest processing window, and favorable mechanical properties.

Applications

  • Exterior components
  • Industrial covers
  • Housings
  • Claddings
  • Shrouds

Properties

  • Property Typical Value Units Test Method
  • Specific Gravitiy 1.09 ISO 1183
  • Gloss, 60°
    (smooth, post-formed, male tooling)     85 - 90 % ASTM 523
  • Crock Mar Resistance
    (Retained gloss at °60 observer)     75-80 % PMC Method
  • Shrink Rate 0.8 – 1.0 % ISO 294-4
  • Flexural Modulus 325,000
    2,241     psi
    MPa     ASTM D790
  • Tensile Strength at Yield 3,825
    26.4     psi
    MPa     ASTM D638
  • Gardner Impact at 32°F (0°C)
    at -22°F (-30°C)     320 (36)
    212 (24)     in*lbs (Joules) ASTM D5420
  • Multi-Axial Impact at 32°F (0°C)
    at -5°F (-15°C)
    at -22°F (-30°C)     38.8, 100% ductile
    46.1, 100% ductile
    30.3, 50% ductile     Joules ASTM D3762
  • HDT at 66 psi (0.45 MPa)
    at 264 psi (1.45 MPa)     205(96)
    124(51)     °F (°C) ASTM D648
  • CLTE (-30°C to 80°C) 3.8 x 10-5
    6.9 x 10-5     in/in/°F
    mm/mm/°C     ISO 11359

*Property values tested on co-extruded sheet, 0.187” thick, 10% cap layer, 30% regrind.157”) thick, 10% cap layer, 30%

NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.