PMC® 1110

PMC® 1110 is a co-extruded sheet comprised of an impact-modified, low gloss acrylic cap over autility ABS core. This product is designed to offer a sheet that provides low gloss & outdoor weather resistance of acrylic, with the favorable economics of utility ABS.

Applications

  • Interior & exterior panels
  • Dashes
  • Consoles
  • Covers
  • Shrouds

Properties

  • Property Typical Value Units Test Method
  • Specific Gravity 1.10 ISO 1183
  • Gloss, 60°
    (textured*, post-formed, male tooling)
    3 - 7 % ASTM 523
  • Shrink Rate 0.5 – 0.7 % ISO 294-4
  • Flexural Modulus 370,000
    2,551
    psi
    MPa
    ASTM D790
  • Tensile Strength at Yield 6,200
    42.8
    psi
    MPa
    ASTM D638
  • Gardner Impact at 73°F (23°C)
    at 32°F (0°C)
    at -22°F (-30°C)
    290(33)
    275(31)
    115(13)
    in*lbs (Joules) ASTM D5420
  • HDT at 66 psi (0.45 MPa)
    at 264 psi (1.45 MPa)
    195 (91)
    180 (82)
    °F (°C) ASTM D648
  • CLTE (-30°C to 80°C) 4.4 x 10-5
    7.9 x 10-5
    in/in/°F
    mm/mm/°C
    ISO 11359

* Property values tested on co-extruded sheet, 0.187” thick, 10% cap layer, up to 30% regrind used.

NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.