ONTEX® 8600
ONTEX® 8600 is directly paintable & bondable sheet system comprised of a thermoformable adhesion film layer (A-side only) laminated to an impact-modified, talc-filled TPO, creating product that has the favorable properties of TPO without the need for surface preparation or special adhesives/coatings. Do not sand this product (will remove the film).
Applications
- Bumpers
- Wheel lips
- Valences
- Claddings
- Rocker panels
- Industrial covers & Enclosures
Properties
- Property Typical Value Units Test Method
- Specific Gravity 1.11 ISO 1183
- Gloss, 60°
(textured, post-formed, male tooling) 7 - 10 % ASTM 523 - Shrink Rate 0.7 – 1.0 % ISO 294-4
- Flexural Modulus 257,297
1,774 psi
MPa ASTM D790 - Tensile Strength at Yield 3,450
23.8 psi
MPa ASTM D638 - Gardner at 32°F (0°C)
Impact at -22°F (-30°C) 320 (36)
300 (34) in*lbs (Joules) ASTM D5420 - HDT at 66 psi (0.45 MPa)
at 264 psi (1.45 MPa) 212 (100)
131 (55) °F (°C) ASTM D648 - CLTE (-30°C to 80°C) 3.3 x 10-5
5.9 x 10-5 in/in/°F
mm/mm/°C ISO 11359
1 Property values tested on an A-side laminated monolithic sheet, 4 mm (0.157”) thick, 30% regrind used
NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification. Rev. 07.20