PMC® 300
PMC® 300 is a high impact, high stiffness monolithic ABS sheet, offering a great balance of rigidity and durability in an easy-to-process product.
Applications
- Interior components
- Shrouds
- Housings & claddings
Properties
- Property Typical Value Units Test Method
- Hardness 77 Shore D ASTM D2240
- Specific Gravity 1.05 ISO 1183
- Gloss, 60°
(textured*, post-formed, male tooling) 5 - 12 % ASTM 523 - Shrink Rate 0.4 – 0.6 % ISO 294-4
- Flexural Modulus 368,000
2,537 psi
MPa ASTM D790 - Tensile Strength at Yield 6,250
43 psi
MPa ASTM D638 - Notched Izod at 73°F (23°C)
Impact at 0°F (-18°C) 8.0 2.8 ft*lb/in ASTM D256 - HDT at 66 psi (0.45 MPa)
at 264 psi (1.45 MPa) 203 (95)
180 (82) °F (°C) ASTM D648 - CLTE (-30°C to 80°C) 4.8 x 10-5
8.6 x 10-5 in/in/°F
mm/mm/°C ISO 11359 - Burn Rate 40 mm/min FMVSS302
* Textured gloss noted. Non-textured (smooth) use of this product not recommended. Color & Texture can affect post-formed gloss rating. Property values tested on monolithic extruded sheet, 0.180 in. (4.6 mm) thick, 30% regrind used.
NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.