PMC® 1150
PMC 1150 is a coextruded sheet comprised of an impact-modified, high gloss acrylic cap over a utility ABS core. This product is designed to offer a sheet that provides the durability & outdoor weather resistance of acrylic, with the ease of processing & bonding of ABS.
Applications
- Interior & exterior panels
- Dashes
- Consoles
- Covers
- Shrouds
Properties
- Property Typical Value Units Test Method
- Specific Gravity 1.10 ISO 1183
- Gloss, 60°
(smooth, post-formed, male tooling) 75 - 90 % ASTM 523 - Shrink Rate 0.5 – 0.7 % ISO 294-4
- Flexural Modulus 370,000
2,551 psi
MPa ASTM D790 - Tensile Strength at Yield 6,047
41.7 psi
MPa ASTM D638 - Gardner at 73°F (23°C) Impact
at 32°F (0°C)
at -22°F (-30°C) 290 (33)
275 (31)
115 (13) in*lbs (Joules) ASTM D5420 - HDT at 66 psi (0.45 MPa)
at 264 psi (1.45 MPa) 195 (91)
180 (82) °F (°C) ASTM D648 - CLTE (-30°C to 80°C) 4.4 x 10⁻⁵
7.8 x 10⁻⁵ in/in/°F
mm/mm/°C ISO 11359
Property values tested on co-extruded sheet, 0.187” thick, 10% cap layer, up to 30% regrind used
NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification. Rev. 03.20