PremierCap® 1650

PremierCap® 1650 is a next-generation high gloss, coextruded TPO sheet system over a standard melt strength core. This product is designed to offer a weatherable cap that provides enhanced scratch & mar resistance over a cost-effective substrate, providing enhanced surface durability with improved economics.

Applications

  • Exterior components
  • Industrial covers
  • Housings
  • Claddings
  • Shrouds

Properties

  • Property Typical Value Units Test Method
  • Specific Gravitiy 1.07 ISO 1183
  • Gloss, 60°
    (textured, post-formed, male tooling)
    85 - 90 % ASTM 523
  • Crock Mar Resistance
    (Retained gloss at 60° observer)
    75 - 80 % PMC Method
  • Shrink Rate 0.8 – 1.0 % ISO 294-4
  • Flexural Modulus 181,250
    1,250
    psi
    MPa
    ASTM D790
  • Tensile Strength at Yield 2,219
    15.3
    psi
    MPa
    ASTM D638
  • Gardner Impact at 32°F (0°C)
    at -22°F (-30°C)
    205 (22.9)
    158 (17.6)
    in*lbs (Joules) ASTM D5420
  • Multi-Axial Impact at 32°F (0°C)
    at -5°F (-15°C)
    at -22°F (-30°C)
    28.2, 100% ductile
    41.0, 100% ductile
    18.7, 0% ductile
    Joules ASTM D3762
  • HDT at 66 psi (0.45 MPa)
    at 264 psi (1.45 MPa)
    189(87)
    118(48)
    °F (°C) ASTM D648
  • CLTE (-30°C to 80°C) 4.4 x 10-5
    8.0 x 10-5
    in/in/°F
    mm/mm/°C
    ISO 11359

*Property values tested on co-extruded sheet, 0.125” thick, 10% cap layer, 30% regrind

NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.