ONTEX® 8765
Ontex® 8765 is a directly paintable & bondable sheet system comprised of a thermoformable adhesion film layer (B side) laminated to an ultra high melt strength, impact-modified, talc-filled TPO core and capped on the A side with PremierCap® high gloss TPO. The result is a product with all of the favorable properties of TPO plus enhanced melt strength as well as a high gloss, enhanced scratch & mar resistant cap and no need for surface preparation or special adhesives for B side bonding. Do not sand this product (will remove the film layer).
Applications
- Bumpers
- Wheel lips
- Valences
- Helms
- Industrial covers & Enclosures
Properties
- Property Typical Value Units Test Method
- Specific Gravity 1.11 ISO 1183
- Gloss, 60°
(smooth, post-formed, male tooling) 85 - 90 % ASTM 523 - Crock Mar Resistance
(Retained gloss at 60° observer) 75 - 80 % PMC Method - Shrink Rate 0.8 – 1.0 % ISO 294-4
- Flexural Modulus 325,000
2,240 psi
MPa ASTM D790 - Tensile Strength at Yield 2,740
18.9 psi
MPa ASTM D638 - Gardner at 32°F (0°C)
Impact at -22°F (-30°C) 320 (35.6)
212 (24) in*lbs (Joules) ASTM D5420 - Multi-Axial at 32°F (0°C)
Impact at -22°F (-30°C) 38.0, 100% ductile
30.3, 50% ductile Joules ASTM D3762 - HDT at 66 psi (0.45 MPa)
at 264 psi (1.45 MPa) 205 (96)
124 (51) °F (°C) ASTM D648 - CLTE (-30°C to 80°C) 3.8 x 10-5
6.9 x 10-5 in/in/°F
mm/mm/°C ISO 11359
NOTE: Data values are typical properties and are not to be construed as specifications. Users should confirm results by their own tests and evaluation methods. SIMONA PMC makes no warranties, expressed or implied, concerning the suitability of use. No freedom from infringement of any patent of others is to be inferred. SIMONA PMC reserves the right to make additions, deletions, or modifications to this information at any time without prior notification.